Effects of Wood Fiber Characteristics on Mechanical Properties of Wood/Polypropylene Composites

Authors

  • Nicole M. Stark
  • Robert E. Rowlands

Keywords:

Wood flour, wood fiber, polypropylene, mechanical properties, aspect ratio, coupling agent

Abstract

Commercial wood flour, the most common wood-derived filler for thermoplastics, is produced in a mixture of particle sizes and generally has a lower aspect ratio than wood and other natural fibers. To understand how wood flour and fiber characteristics influence the mechanical properties of polypropylene composites, we first investigated the effect of different sizes of wood flour particles on the mechanical properties of wood-flour-filled polypropylene composites. We then compared the properties of wood-flour-filled composites to those of composites reinforced with refined wood fiber. We also studied the effect of a maleated polypropylene coupling agent on composite properties. Wood flour particles (35, 70, 120, and 235 mesh) were compounded at 40% by weight with polypropylene. Increases in tensile and flexural strength and modulus of the wood flour composites were found to correspond with increases in aspect ratio. Notched impact energy increased with increasing particle size, whereas unnotched impact energy decreased with increasing particle size. Refined wood fiber and 40-mesh wood flour was compounded at 20% and 40% by weight with polypropylene. Wood fiber resulted in higher strengths at both filler levels and higher moduli at the 40% level compared to the strength properties of wood flour composites. The higher aspect ratio of the wood fiber had little effect on impact energy. The maleated polypropylene coupling agent caused greater strength increases in wood fiber composites than in wood flour composites. The coupling agent did not significantly affect tensile or flexural moduli. Our results clearly support the use of higher aspect ratio wood fibers and coupling agents for increasing the strength of wood/plastic composites.

References

American Society of Testing and Materials (ASTM). 2000a. Tensile properties of plastics. ASTM D638. Annual Book of ASTM Standards. American Society for Testing and Materials, Philadelphia, PA.nAmerican Society of Testing and Materials (ASTM). 2000b. Flexural properties of unreinforced and reinforced plastics and electrical insulating materials. ASTM D790. Annual Book of ASTM Standards. American Society for Testing and Materials, Philadelphia, PA.nAmerican Society of Testing and Materials (ASTM). 2000c. Impact resistance of plastics and electrical insulating materials. ASTM D256. Annual Book of ASTM Standards. American Society for Testing and Materials. Philadelphia, PA.nEckert, C. 2000. Opportunities for natural fibers in plastic composites. In Proc. Progress in Wood Fiber-Plastic Composites Conference; May 25-25, 2000. Toronto, ON.nGauthier, R., H. Gauthier, and C.Joy. 1999. Compatibilization between lignocellulosic fibers and a polyolefine matrix. In Proc. 5th International Conference on Wood Fiber-Plastic Composites; May 26-27, 1999. Madison, WI.nOsswald, T. A. 1999. Fundamental principles of polymer composites: Processing and design. In Proc. 5th International Conference on Wood Fiber-Plastic Composites; May 26-27, 1999. Madison, WI.nOsswald, T. A, and G. Menges. 1995. Materials science of polymers for engineers. Hanser/Gardner Publications, Inc., Cincinnati, OH. 475 pp.nSanadi, A. R., K. Walz, L. Wieloch, R. E. Jacobson, D. F. Caulfield, and R. M. Rowell. 1995. Effect of matrix modification on lignocellulosic composite properties. In Proc. 3rd International Conference on Wood Fiber- Plastic Composites; May 1-3, 1995. Madison, WI.nZaini, M. J., M. Y. A. Faud, Z. Ismail, M. S. Mansor, and J. Mustafah. 1996. The effect of filler content and size on the mechanical properties of polypropylene/oil palm wood flour composites. Polym. Int.40:51-55.n

Downloads

Published

2007-06-05

Issue

Section

Research Contributions