The Effect of Some Process Variables on the Lap-Shear Strength of Aspen Strands Uniformly Coated with pMDI-Resin

Authors

  • Gregory D. Smith

Keywords:

Processing window, resin level, moisture content, press temperature, bond time, pMDI, OSB

Abstract

The effect of bond time, resin level, moisture content, and press temperature on the lap-shear strength of hot-pressed specimens coated with polymeric diphenyl methane diisocyanate (pMDI) has been examined. The strength was found to increase with press temperature, bond time, and moisture content, but decrease with resin level. It was concluded that significant moisture is necessary to obtain high bond strengths. A significant open assembly time effect was also noted with lap-shear strengths increasing with open time.

References

American Society of Testing and Materials (ASTM). 2000. Standard Test Method for Evaluating Properties of Wood-Base Fiber and Particle Panel Materials. D1037. American Society of Testing and Materials, Philadelphia, PA.nBao, S., W. A. Danuch, Y. Sun, P. L. Rinaldi, J. J. Marcinko, and C. C. Phanopoulos. 2003. Solid state two-dimensional NMR studies of polymeric diphenylmethane diisocyanate (PMDI) reaction in wood. Forest Prod. J.53(6):63-71.nChelak, W., and W. H. Newman. 1991. MDI high moisture content bonding mechanism, parameters, and benefits using MDI in composite wood products. Pages 205-229 in T. M. Maloney, ed. Proc. 25th International Particleboard/Composite Material Symposium. Washington State University, Pullman, WA.nFrazier, C., and J. Ni. 1998. On the occurrence of network interpretation in the wood-isocyanate adhesive interphase. Int. J. Adhes. Adhes.18(2):81-87.nFrazier, C., R. Schmidt, and J. Ni. 1996. Towards a molecular understanding of the wood-isocyanate adhesive bondline. Pages 383-391 in Proc. Third Pacific Rim Bio-based Composites Symposium. Dec. 2-5, Kyoto, Japan.nHumphrey, P. E., and D. Zavala. 1989. A technique to evaluate the bonding reactivity of thermosetting adhesives. J. Testing Evol.17:323-328.nMarcinko, J. J., S. Devathala, P. L. Rinaldi, and S. Bao. 1998. Investigating the molecular and bulk dynamics of PMDI/wood and UF/wood composites. Forest Prod. J.48(6):81-84.nMarcinko, J. J., P. L. Rinaldi, and S. Bao. 1999. Exploring the physicochemical nature of PMDI/wood structural wood composite adhesion. Forest Prod. J.49(5):75-78.nNi, J., and C. E. Frazier. 1998. 15N/MAS NMR study of the isocyanate/wood adhesive bondline. Effects of structural isosmerism. J. Adhesion66:89-116.nRosthauser, J. W., K. W. Haider, R. N. Hunt, and W. S. Gustavich. 1997. Chemistry of polymeric MDI wood binders-model studies. Pages 161-175 in T.M. Maloney, ed. Proc. 31st International Particleboard/Composite Material Symposium. Washington State University, Pullman, WA.nSmith, G. D. 2003. The lap-shear strength of droplet arrays of a PF-resin on OSB strands. Forest Prod. J. (53:11/12).nWendler, S. L., and C. E. Frazier. 1996a. Effect of moisture content on the isocyanate/wood adhesive bondline by N CP/MAS NMR. J. Appl. Polym. Sci.61:775-782.nWendler, S. L., and C. E. Frazier. 1996b. The effect of cure temperature and time on the isocyanate-wood adhesive bondline by N CP/MAS NMR. Int. J. Adhes.16:179-186.nZhou, X., and C. E. Frazier. 2001. Double labeled isocyanate resins for the solid-state NMR detection of urethane linkages to wood. Int. J. Adhes.21:259-264.n

Downloads

Published

2007-06-05

Issue

Section

Research Contributions