Lignin Biodegradation of Nitrogen Supplemented Red Oak (<i>Quercus Rubra</i>) Wood Chips with Two Strains of <i>Phanerochaete Chrysosporium</i>
Keywords:
Lignin, wood chips, Phanerochaete chrysosporium, red oakAbstract
Red oak (Quercus rubra L.) wood chips were treated at two levels of nitrogen content (0.95% and 2.87% N level based on oven-dry wood chips) with either anhydrous liquid ammonia or ammonium nitrate in attempts to enhance the lignin degradation rate of a wild and mutant strain of Phanerochaete chrysosporium. As growth time increased, significant changes in weight loss, alkali solubility, alcohol/benzene extractive content, holocellulose content, and klason lignin content were observed.
Experimental results showed that lignin biodegradation rate of both a wild and a mutant strain of P. chrysosporium was increased by pretreating the wood chips with either liquid ammonia at low levels (0.95% N) or by treating wood chips with additions of ammonium nitrate at the 0.95% N and 2.87% N level. Treating red oak chips with liquid ammonia at the 2.87% N level not only caused a reduction in holocellulose content of red oak wood chips, but also inhibited the growth of both strains of P. chrysosporium during incubation. When ammonium nitrate was added to the red oak wood chips at the 2.97% N level, biodegradation capabilities of the wild strain were suppressed. However, the red oak wood chips treated to the 2.87% N level with ammonium nitrate did not affect the growth of the mutant strain of P. chrysosporium. An increase in lignolytic activity was found to occur using the mutant strain of fungus.
Significant differences in lignin and carbohydrate content of fungus-degraded wood were observed. The wild strain appeared to attack the lignin and carbohydrate constituents of wood simultaneously, resulting in a loss in both components as incubation time increased from 0 to 30 days. However, the mutant strain appeared to attack the lignin constituents while leaving the carbohydrate components largely intact. Comparison between the two strains (30 days of incubation) showed the red oak wood chips degraded by the mutant strain had a higher holocellulose content than did the wood chips degraded by the wild strain. These results suggest that the mutant strain may be the preferred fungus to use in manufacturing biomechanical pulps and the biodegradation rate may be slightly increased with the addition of nitrogen to the substrate.
References
American Society for Testing and Materials. 1980. One percent caustic soda solubility of wood. ASTM D 1109-56.nBar-Lev, S. S., T. K. Kirk, and H. Chang. 1982. Evidence that fungal pretreatment can reduce the energy requirement for secondary refining of thermomechanical pulp. TAPPI 65(10):111-113.nChang, H. C. P. 1987. Enzymatic degradation of liquid ammonia pretreated wood. Ph.D. thesis, The Pennsylvania State University, University Park, PA. 191 pp.nChou, Y-C. T. 1987. Supercritical ammonia pretreatent of lignocellulosic material. Pages 21-32 in Biotechnology and bioengineering symposium. No. 17.nEriksson, K. E., and L. Vallander. 1980Biomechanical pulping. Pages 213-233, vol. 2, in Lignin biodegradation: Microbiology, chemistry, and potential applications.nHighley, T. L. 1987. Effect of carbohydrate and nitrogen on hydrogen peroxide formation by wood decay fungi in solid medium. FEMS Microbio. Let. 48:373-377.nJodon, M. H., and D. J. Royse. 1979. Care and handling of cultures of the cultivated mushroom. College of Ag. Ext. Ser. Circular 258. The Pennsylvania State University, University Park, PA.nLeatham, G. F., and T. K. Kirk. 1983. Regulation of lignolytic activity by nitrogen in white rot. FEMS Microbio. Let. 48:373-377.nLeatham, G. F., and G. C. Myers. 1990. A PFI mill can be used to predict biomechanical pulp strength properties. TAPPI 73(4):192-197.nLeatham, G. F., G. C. Myers, and T. H. Wegner. 1990. Biomechanical pulping of aspen chips: Energy savings resulting from different fungal treatments. TAPPI 73(5):197-200.nOriaran, T. P. 1989. Kraft pulp and papermaking properties of Phanerochaete chrysosporium degraded aspen (Populus tremulodies) and red oak (Quercus rubra). Ph.D. dissertation, The Pennsylvania State University, University Park, PA. 175 pp.nRyan, T. A., B. L. Joiner, and B. F. Ryan. 1986. Minitab student handbook. Duxbury Press, North Scituate, MA.nSAS Institute. 1983. SAS user's guide. SAS Institute Inc., Cary, NC. 199 pp.nTien, M., and S. B. Myer. 1990. Mutants of Phanerochaete chrysosporium exhibiting ligninolytic activity under nutrient-rich conditions: Selection and characterization of (submitted for publication).nTrotter, C. P. 1990a. Biotechnology in the pulp and paper industry: A review. Part 1: Tree improvement, pulping and bleaching and dissolving pulp application. TAPPI 73(4):198-203.nTrotter, C. P. 1990b. Biotechnology in the pulp and paper industry: A review. Part 2: Upgrading pulp properties, papermaking, effluent treatment, and converting biomass to fuels and chemicals. TAPPI 73(5):201-205.nWang, P. E., H. J. Boker, and C. B. Purves. 1964. Ammonolysis of uronic ester groups in birch xylan. Can. J. Chem. 42(11):2434-2439.nWaiss, A. C., J. Guggolz, G. D. Kohles, and H. G. Walker. 1972. Improving digestibility of straw for ruminant feed by aqueous ammonia. J. Animal Sci. 35(1):109-112.n
Downloads
Published
Issue
Section
License
The copyright of an article published in Wood and Fiber Science is transferred to the Society of Wood Science and Technology (for U. S. Government employees: to the extent transferable), effective if and when the article is accepted for publication. This transfer grants the Society of Wood Science and Technology permission to republish all or any part of the article in any form, e.g., reprints for sale, microfiche, proceedings, etc. However, the authors reserve the following as set forth in the Copyright Law:
1. All proprietary rights other than copyright, such as patent rights.
2. The right to grant or refuse permission to third parties to republish all or part of the article or translations thereof. In the case of whole articles, such third parties must obtain Society of Wood Science and Technology written permission as well. However, the Society may grant rights with respect to Journal issues as a whole.
3. The right to use all or part of this article in future works of their own, such as lectures, press releases, reviews, text books, or reprint books.