Evaluation of Tensile Fracture in Aspen Using Fractographic and Theoretical Methods

Authors

  • John A. Akande
  • George H. Kyanka

Keywords:

Ray, fracture toughness, brown rot, white rot, decay weight loss

Abstract

Based on the linear elastic fracture mechanics (LEFM) concept, apparent mode I fracture toughness KIcLR was calculated for unnotched aspen (Populus tremuloides Michx.) specimen (5 in. x 0.188 in. x 0.094 in. dimension) tested in tension parallel to grain. The purpose was to relate wood fracture toughness to average ray spacing. Observations along the longitudinal-radial plane of fracture showed the ray/fiber interface as a notable zone of crack propagation. Step-like progression of fracture lines occurred from one ray to another thus leading to an hypothesis that the average ray spacing could reasonably estimate the critical flaw dimension. Using this model, the calculated kIcLR was close to available published data. In additional experiments, it was revealed that kIcLR is sensitive to decay weight losses. Within 2% to 16% weight loss examined, loss of kIcLR was found to be more pronounced with a brown rot fungus when compared to white rot fungi.

References

American Society for Testing and Materials (ASTM). 1988a. Standard method of accelerated laboratory test of natural decay resistance of woods. D 2017-81/86. Annual book of ASTM standards. Construction. Section 4, vol. 04.09 Wood, Philadelphia, PA, pp. 323-326.nAmerican Society for Testing and Materials (ASTM). 1988b. Standard test methods for specific gravity of wood and wood-base materials. D 2395-69/77. Annual book of ASTM standards. Construction. Section 4, vol. 04.09 Wood, Philadelphia, PA, pp. 359-366.nBariska, M., and L. J. Kucera. 1985. On the fracture morphology in wood. Part 2: Macroscopic deformations upon ultimate axial compression in wood. Wood Sci. Technol. 19:19-34.nCôté, W. A., and R. B. Hanna. 1983. Ultrastructural characteristics of wood fracture surfaces. Wood Fiber Sci. 15(2):135-163.nDebaise, G. R., A. W. Porter, and R. E. Pentoney. 1966. Morphology and mechanics of wood fracture. Materials Res. Stand. 6:493-499.nGriffith, A. A. 1925. Proceeding of the 1st International Congress for Applied Mechanics. Delft (Waltman). 55 pp.nIrwin, G. P. 1957. Analysis of stresses and strains near the end of a crack traversing a plate. J. Appl. Mech. 57(22):361-364.nJeronimidis, G. 1976. The fracture of wood in relation to its structure. Leiden Botanical Service 3: 253-265.nJung, J., and J. F. Murphy. 1983. An investigation of the fracture of butt joints in parallel-laminated veneer 1. Wood Fiber Sci. 15(2): 116-134.nKeith, C. T. 1971. The anatomy of compression failure in relation to creep-inducing stresses. Wood Science 4:71-82.nKeith, C. T. 1974. Longitudinal compressive creep and failure development in white spruce compression wood. Wood Science 7:1-12.nKeith, C. T., and W. A. Cote. 1968. Microscopic characterization of slip lines and compression failures in wood cell walls. Forest Prod. J. 18(3):67-74.nMurphy, J. F. 1978. Using fracture mechanics to predict failure in notched wood beams. Proceedings, 1st International Conference on Wood Fracture. Banff, Alberta, pp. 159-173.nPatton-Mallory, M., and S. M. Cramer. 1987. Fracture mechanics: A tool for predicting wood components strength. Forest Prod. J. 37(7/8):39-47.nPellicane, P. J., J. Bodig, and J. R. Goodman. 1982. Simulation of the tensile strength-fracture toughness relationship. Wood Science 14(4): 168-177.nPorter, A. W. 1964. On the mechanics of fracture in wood. Forest Prod. J. 13:325-331.nSchniewind, A. P., and J. C. Centeno. 1973. Fracture toughness and duration of load factor 1. Six principal systems of crack propagation and duration factor for crack propagating parallel to grain. Wood Fiber 5(2): 152-159.nSiau, J. F. 1971. Flow in wood. Syracuse University Press, Syracuse, NY, 131 pp.nSinclair, S. A., G. Ifju, and J. A. Johnson. 1978. Changes in toughness of wood from beetle-killed shortleaf pine. Forest Prod. J. 28(7):44-47.nSmith, F. W., and D. T. Penny. 1980. Fracture mechanics analysis of butt joints in laminated wood beams. Wood Science 12(4):227-235.nTada, H., P. C. Paris, and G. R. Irwin (ED.). 1973. Stress analysis of cracks handbook. Del Research Corp. Hellertown, PA.nWilliams, J. G., and M. W. Birch. 1976. Mixed mode fracture in anisotropic media. ASTM, 1916 Race Str. Phil., PA 19103. Technical Bulletin 601:125-137.n

Downloads

Published

2007-06-22

Issue

Number 3 / July 1990

Section

Research Contributions

License

The copyright of an article published in Wood and Fiber Science is transferred to the Society of Wood Science and Technology (for U. S. Government employees: to the extent transferable), effective if and when the article is accepted for publication. This transfer grants the Society of Wood Science and Technology permission to republish all or any part of the article in any form, e.g., reprints for sale, microfiche, proceedings, etc. However, the authors reserve the following as set forth in the Copyright Law:

1. All proprietary rights other than copyright, such as patent rights.

2. The right to grant or refuse permission to third parties to republish all or part of the article or translations thereof. In the case of whole articles, such third parties must obtain Society of Wood Science and Technology written permission as well. However, the Society may grant rights with respect to Journal issues as a whole.

3. The right to use all or part of this article in future works of their own, such as lectures, press releases, reviews, text books, or reprint books.